- TORESERAM*R* beads and balls are mainly made of tetragonal zirconia that provides the largest strength of all ceramics thanks to yttrium oxide added to zirconia.
- It contains almost no SiO*@2@*, Fe*@2@*O*@3@*, and MgO that cause contamination.
Spec
- Chemical composition: ZrO2 (including HfO2)/94.75 +/- 0.60wt%, Y2O3/4.90 +/- 0.50wt%, Al2O3/0.30 +/- 0.10wt%
- Density: 6.0g/mL
- Hardness (vickers hardness): HV1150-1200
- Young's Modulus: 210 - 220GPa
- Bend strength: 1000MPa
- Average crystal piece diameter: 0.3 - 0.4μm
- Capacity: 1kg
- Diameter (φmm): 2.35
- Trayceram R
- Application: Electronic part material, Electronic material, Inorganic powder such as fine ceramics, Magnetic paint, Ink, pigment, paint, Thermosensitive material
Package size：160×150×110 mm 1.1 kg